Organocatalytic acetylation of pea starch was systematically optimized using tartaric acid as catalyst. The effect of the degree of substitution with alkanoyl (DSacyl) and tartaryl groups (DStar) on thermal and moisture resistivity, and film-forming properties was investigated. Pea starch with DSacyl from 0.03 to 2.8 was successfully developed at more efficient reaction rates than acetylated maize starch. Nevertheless, longer reaction time resulted in granule surface roughness, loss of birefringence, hydrolytic degradation, and a DStar up to 0.5. Solid-state 13C NMR and SEC-MALS-RI suggested that tartaryl groups formed crosslinked di-starch tartrate. Acetylation increased the hydrophobicity, degradation temperature (by ~17 %), and glass transition temperature (by up to ~38 %) of pea starch. The use of organocatalytically-acetylated pea starch with DSacyl ≤ 0.39 generated starch-based biofilms with higher tensile and water barrier properties. Nevertheless, at higher DS, the incompatibility between highly acetylated and native pea starches resulted in a heterogenous/microporous structure that worsened film properties.
Keywords: Biofilms; Chromatography; NMR; Organocatalytic esterification; Packaging; Tartaric acid.
Copyright © 2022 The Authors. Published by Elsevier Ltd.. All rights reserved.