Purpose: A novel implant model consisting of meso-scale cactus-inspired spikes and nano-scale bone-inspired trabeculae was recently developed to optimize meso-scale roughness on zirconia. In this model, the meso-spike dimension had a significant impact on osteoblast function. To explore how different nano-textures impact this model, here we examined the effect of different nano-trabecula sizes on osteoblast function while maintaining the same meso-spike conformation.
Methods: Zirconia disks with meso-nano hybrid surfaces were created by laser etching. The meso-spikes were fixed to 40 μm high, whereas the nano-texture was etched as large and small trabeculae of average Feret diameter 237.0 and 134.1 nm, respectively. A polished surface was also prepared. Rat bone marrow-derived and human mesenchymal stromal cell-induced osteoblasts were cultured on these disks.
Results: Hybrid rough surfaces, regardless of nano-trabecula dimension, robustly promoted the osteoblastic differentiation of both rat and human osteoblasts compared to those on polished surfaces. Hybrid surfaces with small nano-trabeculae further enhanced osteoblastic differentiation compared with large nano-trabeculae. However, the difference in osteoblastic differentiation between small and large nano-trabeculae was much smaller than the difference between the polished and hybrid rough surfaces. The nano-trabecula size did not influence osteoblast attachment and proliferation, or protein adsorption. Both hybrid surfaces were hydro-repellent. The atomic percentage of surface carbon was lower on the hybrid surface with small nano-trabeculae.
Conclusions: Small nano-trabeculae promoted osteoblastic differentiation more than large nano-trabeculae when combined with meso-scale spikes. However, the biological impact of different nano-trabeculae was relatively small compared with that of different dimensions of meso-spikes.
Keywords: Cactus; Implants; Laser etching; Nanotechnology; Osseointegration.