Objective: The aim of the study was to evaluate the tensile BS of FPs luted with conventional and self-adhesive resin modified GIC cement on disinfection of post-space radicular dentin with various photo-activated photosensitizer (chitosan, TB and Clp6).
Materials and methods: Sixty-six orthodontically extracted mandibular pre-molars were selected on specific exclusion/inclusion criteria, trailed by thorough debridement of plaque/calculus and disinfected by immersion in Chloramine T trihydrate solution for 48 hrs. The selected teeth were sectioned from the cement-enamel junction removing the crown. The radicular region of the samples was entrenched perpendicularly in heat cure resin modified acrylic. The pulpal tissue was detached using K-files trailed by canal shaping with ProTaper Next rotary NiTi (Dentsply Sirona, Gloucestershire, UK) files under continuous irrigation with NaOCl. The canals were dried using paper points trailed by obturation by Pro Taper Next Obturators gutta-percha points (Dentsply, UK) coated with ADSEAL (Meta Biomed, Chungcheongbuk-do, South Korea). After incubation for seven days in an environment mimicking oral cavity, post space was created using peso reamers. The space was disinfected by G1: chitosan 3 mg/mL; G2: 13-15 mg/mL TB and G3: Clp6. After photo-irridation the FPs were luted with conventional (n=11) and resin modified self-adhesive cement (n=11) for each group respectively. The specimens were incubated for 48 hrs prior to tensile BS testing. The type of bond fracture/failure was evaluated under 30x magnification. The tensile BS was statistically analyzed using ANOVA trailed by Tukey's test to respective groups.
Results: FPs luted using self-adhesive resin modified cement with prior to disinfection by TBs displayed highest tensile BS 291.47 N ± 5.36. On the contrary, post-space disinfected by Clp6 displayed statistically significant (p ≤ 0.05) lowest bond strength (276.62 N ± 4.31). Intra-group analysis displayed statistically significant difference in bond strength of the luting dental materials (p ≤ 0.05).
Conclusions: The self-adhesive resin modified cement revealed utmost bond strength on pre-treatment of post-space with respective photo-activated photosensitizer (chitosan, TB & Clp6) in contrast to conventional GIC.