Lithium-sulfur batteries (LSBs) have been considered promising candidates for next-generation energy storage devices owing to their high energy density, low price, and environment-friendly characteristics. However, their commercialization has been hindered by the "shuttle effect", which occurs during the charge/discharge cycles and leads to poor cycling performance and low coulombic efficiency. Here, we synthesized flower-shaped hollow VOOH spheres on the carbon nanotube (CNT) network, which were used as the multifunctional sulfur host materials for the first time in LSBs. These VOOH spheres can chemically and physically confine polysulfides as well as catalyze their redox conversion; additionally, their hollow structure can effectively accommodate the volume change during cycling. Moreover, the CNTs among spheres can improve the conductivity of the host material and increase the number of active sites for interfacial reactions. Accordingly, when used as a cathode material, VOOH@CNTs/S composites exhibited a large specific discharge capacity of 1414.63 mAh/g at 0.1 C and excellent cycling stability. At a low current density of 0.5 C, VOOH@CNTs/S exhibited a capacity decay of 0.044% per cycle after 100 cycles. Importantly, at an ultrahigh current density of 5 C, a specific capacity as high as 455.09 mAh/g could be still be delivered after 1000 cycles, corresponding to a superior capacity retention of 90.46% and an ultralow capacity decay of 0.009% per cycle. These findings open up a new material for the practical application of LSBs with ultrafast charge/discharge property and long-lasting cyclic stability.
Keywords: Li−S batteries; absorption; catalyzation; hollow spheres/carbon nanotubes; metal oxyhydroxide; superior cyclic performance.