Promotional effect of Ca doping on Bi2Fe4O9 as peroxymonosulfate activator for gatifloxacin removal

Abstract

A series of Ca-doped bismuth ferrite was prepared at various %w/w of Ca via a facile hydrothermal method to obtain Bi_2XCa_2(1-X)Fe₄O₉ (denoted as BFOCa-X, where X = 1, 0.95, 0.90, 0.80, 0.50). The BFOCa-X catalysts were characterized, and the results showed that they consist of pure phase BFO with nanosheet-like morphology. The as-prepared BFOCa-X catalysts were used as peroxymonosulfate (PMS) activator for gatifloxacin (GAT) removal. It was found that the catalytic activity decreased in the following order: BFOCa-0.8 (90.2% GAT removal efficiency in 45 min, k_app = 0.084 min^-1)>BFOCa-0.95 > BFOCa-0.9 > BFOCa-0.5 > BFO indicating that BFOCa-0.8 has the optimized active sites for catalysis. The Ca dopant contributed to the increased oxygen vacancies and surface hydroxyl groups, promoting the catalytic PMS activation process. The k_app value increased gradually with increasing catalyst loading and PMS dosage while pH 9 presented the highest GAT removal rate. The GAT degradation rate was inhibited by PO₄³-, humic acid and NH₄⁺ but promoted in the presence of Cl-, NO₃- and HCO₃-. It was also found that the GAT can undergo several degradation pathways in the catalytic PMS system, which eventually mineralized into innocuous compounds. The dominant reactive oxygen species (ROS) were identified using chemical scavengers, revealing that SO₄^•-, ¹O₂ and ^•OH contributed significantly to GAT degradation. Based on the XPS study, PMS was activated by the Fe²⁺/Fe³⁺ redox cycling and oxygen vacancies to produce SO₄^•-/^•OH and ¹O₂, respectively. Overall, the BFOCa-0.8 also showed excellent reusability up to at least 4 cycles with low Bi and Fe leaching (<7 and 62 μg L^-1, respectively), indicating that it has promising potential for application as PMS activator for antibiotics removal.

Keywords: Bismuth ferrite; Calcium doping; Gatifloxacin; Oxygen vacancies; Peroxymonosulfate; Sulfate radicals.