The effects of green tea extract (GTE) at varying concentrations (0.000, 0.125, 0.250, 0.500, and 1.000%, w/v) on the properties of rice-starch-pectin (RS-P) blend films were investigated. The results showed that GTE addition enhanced (p < 0.05) the antioxidation properties (i.e., total phenolic content, DPPH radical scavenging activity, and ferric reducing antioxidant power) and thickness of the RS-P composite film. The darker appearance of the RS-T-GTE blend films was obtained in correspondence to the lower L* values. However, the a* and b* values were higher toward red and yellow as GTE increased. Though GTE did not significantly alter the film solubility, the moisture content and the water vapor permeability (WVP) of the resulting films were reduced. In addition, the GTE enrichment diminished the light transmission in the UV-Visible region (200−800 nm) and the transparency of the developed films. The inclusion of GTE also significantly (p < 0.05) lowered the tensile strength (TS) and elongation at break (EAB) of the developed film. The FT-IR spectra revealed the interactions between RS-P films and GTE with no changes in functional groups. The antimicrobial activity against Staphylococcus aureus (TISTR 764) was observed in the RS-P biocomposite film with 1% (w/v) GTE. These results suggested that the RS-P-GTE composite film has considerable potential for application as active food packaging.
Keywords: active film; antioxidant; green tea extract; pectin; rice starch.