The ablation mechanism and performance of carbon fiber (CF)-reinforced poly aryl ether ketone (PAEK) thermoplastic composites were studied in this paper. The results show that the ablation damaged area is controlled by the irradiation energy, while the mass loss rate is controlled by the irradiation power density. In the ablation center, the PAEK resin and CFs underwent decomposition and sublimation in an anaerobic environment. In the transition zone, the resin experienced decomposition and remelting in an aerobic environment, and massive char leaves were present in the cross section. In the heat-affected zone, only remelting of the resin was observed. The fusion and decomposition of the resin caused delamination and pores in the composites. Moreover, oxygen appeared crucial to the ablation morphology of CFs. In an aerobic environment, a regular cross section formed, while in an anaerobic environment, a cortex-core structure formed. The cortex-core structure of CF inside the ablation pit was caused by the inhomogeneity of fibers along the radial direction and the residual carbon layer generated by resin decomposition in an anoxic environment. The description of the ablation mechanism presented in this study broadens our understanding of damage evolution in thermoplastic composites subjected to high-energy CW laser irradiation.
Keywords: ablation mechanism; continuous wave laser; thermoplastic composites.