HR3C (25Cr-20Ni-Nb-N) is a key material used in heat exchangers in supercritical power plants. Its creep properties and microstructural evolution has been extensively studied at or below 650 °C. The precipitation evolution in HR3C steel after creep rupture at elevated temperatures of 700 °C and 750 °C with a stress range of 70~180 MPa is characterized in this paper. The threshold strength at 700 °C and 750 °C were determined by extrapolation method to be σ105700= 57.1 MPa and σ105750=37.5 MPa, respectively. A corresponding microstructure investigation indicated that the main precipitates precipitated during creep exposure are Z-phase (NbCrN), M23C6, and σ phase. The dense Z-phase precipitated dispersively in the austenite matrix along dislocation lines, and remained stable (both size and fraction) during long-term creep exposure. M23C6 preferentially precipitated at grain boundaries, and coarsening was observed in all creep specimens with some continuous precipitation of granular M23C6 in the matrix. The brittle σ phase formed during a relatively long-term creep, whose size and fraction increased significantly at high temperature. Moreover, the σ phases, grown and connected to form a large "island" at triple junctions of grain boundaries, appear to serve as nucleation sites for high stress concentration and creep cavities, weakening the grain boundary strength and increasing the sensitivity to intergranular fracture.
Keywords: HR3C steel; creep rupture; microstructure; precipitates.