In order to solve the problem of poor crack resistance and frost resistance of semi-rigid base, rubber powder and retarder were added to a semi-rigid base mixture. First, 61 mixing ratios were determined. Then, through the unconfined compressive strength, splitting strength, and other tests, the mechanical, crack, and frost resistance properties of the retarded composite semi-rigid base coarse mixture with rubber powder were studied. Finally, the macro and micro properties of the two kinds of admixture composite semi-rigid base coarse mixtures were studied by means of SEM and industrial CT. The results show that rubber powder and retarder can effectively improve the cracking and freezing resistance of the mixture. After five freeze-thaw cycle tests, the strength of the retarded composite semi-rigid base material mixed with rubber powder decreased slightly compared with the mixture without additives. It can be seen that rubber powder improved the frost resistance of the mixture. When the content of rubber powder was 1.5%, the BDR value of the mixture increased by 8.8%. With the increase of unconfined compressive strength, splitting strength, and flexural tensile strength at 28 d and 90 d, it was found that the retarder improved the middle and late strength of the mixture. When the content of retarder was 0.09%, the increase of unconfined compressive strength at 28 d reached 3.9%. The addition of rubber powder and retarder improved the distribution of internal pores, the proportion of large pores decreased, and the proportion of small pores increased. The retarder changed the morphology of hydration products, formed a dense network supporting structure, further refined the pores, and reduced the porosity of the mixture. The proportion of pores with a volume greater than 100 mm3 in the total pore volume decreased by 26.01%, and the proportion of medium pores increased by 13.07%, thereby improving the mechanical properties of the mixture.
Keywords: micro-analysis; retarder; road engineering; rubber powder; semi-rigid base.