This paper aims to investigate the fatigue cracking evolution of cold recycled asphalt mixtures with asphalt emulsion (CRME) under different curing times. The fatigue cracking model of CRME based on damage mechanics and fracture mechanics was analyzed according to the fatigue loading curve. Firstly, the fatigue cracking evolution of CRME was studied through an SCB strength test and SCB fatigue test. Then, the fatigue damage mechanics were used to establish a nonlinear fatigue cracking model, and the damage degree of CRME at the initial cracking point was determined. The Paris formula was used to characterize the law of fatigue crack propagation. Finally, the microstructure of CRME was observed by scanning electron microscopy (SEM) with the backscattering method. The results indicate that the initial cracking point appears at around 60% of the fatigue life according to the SCB fatigue test by means of image analysis. The damage variable was obtained through the cracking model, and the value of the damage variable was determined as 0.06-0.17 at the initial cracking point. In addition, the Paris formula showed that the crack growth of CRME can be reflected by the stress intensity factor and correlative parameters. Moreover, cement hydration products were mixed with the asphalt membrane to form a denser spatial structure during the curing process, which may provide higher fatigue performance of CRME. This research may provide a theoretical reference for studying the fatigue cracking behavior of CRME.
Keywords: SCB test; cold recycled mixtures; fatigue cracking; fatigue damage model.