Biocompatibility and pro-mineralization effect of tristrontium aluminate cement for endodontic use

Sherif Adel; Kentaro Hashimoto; Nobuyuki Kawashima; Takahiro Wada; Motohiro Uo; Takashi Okiji

doi:10.1016/j.jds.2021.12.018

Biocompatibility and pro-mineralization effect of tristrontium aluminate cement for endodontic use

J Dent Sci. 2022 Jul;17(3):1193-1200. doi: 10.1016/j.jds.2021.12.018. Epub 2022 Jan 6.

Authors

Sherif Adel^{1

2}, Kentaro Hashimoto¹, Nobuyuki Kawashima¹, Takahiro Wada³, Motohiro Uo³, Takashi Okiji¹

Affiliations

¹ Department of Pulp Biology and Endodontics, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University (TMDU), Tokyo, Japan.
² Department of Restorative and Dental Materials, Oral and Dental Research Division, National Research Centre of Egypt, Cairo, Egypt.
³ Department of Advanced Biomaterials, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University (TMDU), Tokyo, Japan.

Abstract

Background/purpose: Tristrontium aluminate (S₃A) is a hydraulic cement with setting behavior similar to that of mineral trioxide aggregate (MTA). This study examined the biological effects of S₃A on mouse dental papilla cells (MDPs) in vitro and on rat exposed pulps in vivo.

Materials and methods: Extracts of S₃A and MTA were prepared by immersing each cement in ultrapure water. MDPs were cultured with S₃A or MTA extracts, and cell proliferation was evaluated with a tetrazolium-salt assay. Attachment of MDPs on the set cements was examined with scanning electron microscopy (SEM). mRNA expression of bone morphogenic protein (Bmp2), osteocalcin (Oc) and osteopontin (Opn) in MDPs exposed to S₃A or MTA extracts was determined with reverse transcription-quantitative polymerase chain reaction. Mineralized nodule formation was evaluated with Alizarin Red S staining. Simulated body fluid (SBF)-dipped S₃A was examined with SEM and energy dispersive X-ray analysis (EDX). Exposed molar pulps of male Wistar rats capped with S₃A or MTA were histologically examined.

Results: S₃A extract did not inhibit proliferation of MDPs. Set S₃A and MTA exhibited attachment of MDPs on their surface. S₃A extract showed significantly higher mineralized nodule formation and mRNA expression of Bmp2, Oc, and Opn than did MTA extract. SBF-dipped S₃A exhibited formation of surface precipitates, which were composed of Ca, P, Sr, and Al. Direct pulp capping with S₃A and with MTA induced mineralized tissue repair of the exposed pulp.

Conclusion: S₃A possesses biocompatibility and pro-mineralization effects comparable to those of MTA.

Keywords: Cell attachment; Cell proliferation; Endodontic cement; Mineralization; Odonto/osteogenic differentiation; Strontium aluminate.