Biogas up-gradation is a useful method to control CO2 emission and enhance the green process. The demand for renewable sources is increasing due to the depletion of fossil fuels. Thin-film nanocomposites functionalized with tunable molecular-sieving nanomaterials have been employed to tailor membranes with enhanced permeability and selectivity. In this work, the cellulose nanocrystals as a filler in the polyvinyl alcohol matrix are prepared to achieve high-performance facilitated transport membranes for CO2 capture. Considering the mechanical stability, interfacial compatibility and high moisture uptake of the filler, the main objective of this work was to develop a novel aminated CNC (Am-CNC)/polyvinyl alcohol nanocomposite membrane for biogas upgrading. The hydroxyl groups (O-H) on the reducing end of the cellulose nanocrystals were replaced by amino groups (N-H2). It was discovered through Scanning electron microscopy (SEM), X-ray diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FTIR) that adding Am-CNCs in PVA membranes shows an increment in the CO2 removal and effectively upgrades the biogas. The effect of change in concentration of Am-CNC and feed pressure was investigated. The results showed that with increasing Am-CNC concentration up to 1.5 wt%, the thickness of the selective membrane layer increased from 0.95 to 1.9 μm with a decrease in the moisture uptake from 85.04 to 58.84%. However, the best CO2 permeance and selectivity were achieved at 0.306 m3/m2.bar.h (STP) and 33.55, respectively. Furthermore, there was a more than two-fold decrease in CO2 permeance and a 27% decrease in the CO2/CH4 selectivity when the feed pressure increased from 5 to 15 bar. It was revealed that PVA/Am-CNC membrane is high performing for the biogas upgradation.
Keywords: Biogas upgradation; Cellulose nanocrystals; Facilitated transport membrane and interfacial compatibility; Green process; Nanocomposite membranes; Polyvinyl alcohol.
Copyright © 2022 The Authors. Published by Elsevier Inc. All rights reserved.