Chemical solution deposition (CSD) of BaTiO3 (BT) or BT-based thin films relies on using a carboxylic acid and alcohol as the solvents for alkaline-earth carboxylate and transition-metal alkoxide, respectively; however, the esterification reaction of the solvents may lead to in-situ water formation and precipitation. To avoid such an uncontrolled reaction, we developed a route in which ethylene glycol (EG) is used as the solvent for Ba-acetate. The EG-based BT coating solutions are stable for at least a few months. The thermal decomposition of the BT xerogel obtained by drying the EG-based solutions depends on the choice of the solvent for the Ti-alkoxide as well: in the case of EG and 2-methoxyethanol solvents carbon residues are removed at only about 1100 °C, while in the case of ethanol it is concluded at about 700 °C. About 100 nm thick BT films derived from the EG-ethanol solution deposited on platinized silicon reveal dense, crack-free columnar microstructure. They exhibit local ferro- and piezoelectric properties. The macroscopic polarization-electric field loops were obtained up to a quite high electric field of about 2.4 MV/cm. The EG-ethanol based CSD route is a viable alternative to the established acetic acid-alcohol route for BT and BT-based films.
Keywords: BaTiO3 thin films; chemical solution deposition; crystallinity; ferroelectric; piezoelectric; solvent influence.