Three-point bending tests on Short Beam Shear (SBS) specimens are performed to investigate the interlaminar shear properties of plain weave fabric CFRP composites. The tests are performed in a controlled environmental chamber at two different elevated temperatures. The interlaminar shear properties of the specimens remain largely unaffected by the testing temperature. However, the SEM micrographs show different damage progressions between the specimens tested at 100 °C and 120 °C. Fibre ruptures and longer delamination between the plies, as a result of a high temperature, are observed in the specimens tested at 120 °C, which are not observed in the specimens tested at 100 °C. In addition, the acoustic emission activities during the tests are investigated by using piezoelectric sensors. The information-theoretic parameter, the Lempel-Ziv (LZ) complexity, is calculated for the recorded acoustic signals. The LZ Complexities are used for identifying the occurrence of the first delamination failure in the specimens. Additionally, the two features of the acoustic signals, LZ complexity and Weighted Peak Frequency (W.P-Freq), are used for distinguishing the different damage sources in the CFRP specimens. The results are well-supported by the time-frequency analysis of the acoustic signals using a Continuous Wavelet Transform (CWT).
Keywords: CFRP; Continuous Wavelet Transform; Lempel-Ziv Complexity; SEM micrographs; Short Beam Shear (SBS) Test; acoustic emission; frequency analysis; high-temperature applications; interlaminar shear properties.