Polyethylene terephthalate (PET) is used worldwide for packing, and for this reason, it is the main material in plastic waste. The paper uses granules of recycled PET (R-PET) as raw material for producing filaments for 3D printing, subsequently used for printing the test specimens in different ways: longitudinally and at angles between 10° and 40° in this direction. Both the filaments and the printed specimens experience thermally driven shape memory effect (SME) since they have been able to recover their straight shape during heating, after being bent to a certain angle, at room temperature (RT). SME could be reproduced three times, in the case of printed specimens, and was investigated by cinematographic analysis. Then, differential scanning calorimetry (DSC) was used, in R-PET granules, filaments and 3D printed specimens, to emphasize the existence of glass transition, which represents the governing mechanism of SME occurrence in thermoplastic polymers, as well as a recrystallization reaction. Subsequently, the paper investigated the 3D printed specimens by dynamic mechanical analysis (DMA) using a dual cantilever specimen holder. Temperature (DMA-TS) and isothermal scans (DMA-Izo) were performed, with the aim to discuss the variations of storage modulus and loss modulus with temperature and time, respectively.
Keywords: 3D printing; internal friction; recycled PET; shape memory effect; storage modulus.