In micro-injection molding, the plastic filling in the cavity is limited by the frozen layer due to the rapid cooling of the hot melt when it comes into contact with the surface of the cavity at a lower temperature. This problem is more serious with composite materials, which have a higher viscosity than pure materials. Moreover, this issue is also more serious with composite materials that have a higher weight percentage of glass filer. In this article, a pre-heating step with the internal gas heating method was used to heat the cavity surface to a high temperature before the filling step to reduce the frozen layer and to improve the filling ability of the composite material (polyamide 6 + 30% glass fiber) in the micro-injection molding process. To heat the cavity surface, an internal gas-assisted mold temperature control (In-GMTC) system was used with a pulsed cooling system. We assessed different mold insert thicknesses (t) and gaps between the gas gate and the heating surface (G) to achieve rapid mold surface temperature control. The heating process was observed using an infrared camera, and the temperature distribution and the heating rate were analyzed. Thereafter, along with the local temperature control, the In-GMTC was used for the micro-injection molding cycle. The results show that, with a gas temperature of 300 °C and a gas gap of 3.5 mm, the heating rate reached 8.6 °C/s. The In-GMTC was also applied to the micro-injection molding process with a part thickness of 0.2 mm. It was shown that the melt flow length had to reach 24 mm to fill the cavity completely. The results show that the filling ability of the composite material increased from 65.4% to 100% with local heating at the melt inlet area when the gas temperature rose from 200 to 400 °C with a 20 s heating cycle.
Keywords: dynamic mold temperature control; injection molding; internal gas-assisted mold temperature control; melt flow length; micro-injection molding product; mold heating.