Binder jetting is a layer-based additive manufacturing process for three-dimensional parts in which a print head selectively deposits binder onto a thin layer of powder. After the deposition of the binder, a new layer of powder is applied. This process repeats to create three-dimensional parts. The binder jetting principle can be adapted to many different materials. Its advantages are the high productivity and the high degree of freedom of design without the need for support structures. In this work, the combination of binder jetting and casting is utilized to fabricate metal parts. However, the achieved properties of binder jetting parts limit the potential of this technology, specifically regarding surface quality. The most apparent surface phenomenon is the so-called stair-step effect. It is considered an inherent feature of the process and only treatable by post-processing. This paper presents a method to remove the stair-step effect entirely in a binder jetting process. The result is achieved by controlling the binder saturation of the individual voxel volumes by either over or underfilling them. The saturation is controlled by droplet size variation as well as dithering, creating a controlled migration of the binder between powder particles. This work applies the approach to silica sand particle material with an organic binder for casting molds and cores. The results prove the effectiveness of this approach and outline a field of research not identified previously.
Keywords: 3D printing; additive manufacturing; binder jetting; casting; dithering; finishing; grayscale; sand printing; stair-steps; surface quality.