The neutralization process of carbon steel pickling wastewater produces a large amount of steel hydrochloric acid pickling sludge (SHPS), and improper treatment of this sludge poses a serious threat to the environment. Considering that SHPS contains a large amount of iron oxide and given the huge demand for iron concentrate in China's ironmaking industry, refining iron oxide in SHPS into iron concentrate will have great environmental and economic benefits. This paper proposes a new method that uses biomass (corncob) to replace conventional coal-based reductants for the recovery of iron components in SHPS to simultaneously utilize two kinds of solid waste resources. Factors that affect the iron recovery rate and iron grade of SHPS, such as the reaction temperature, corncob dosage, residence time, and magnetic field strength, were studied using a fixed bed and a magnetic separator. These studies were combined with thermodynamic analysis, thermogravimetric analysis, X-ray diffraction, inductively coupled plasma-mass spectrometry, gas chromatography, etc. The results showed that when the reaction temperature was 680 °C, the corncob dosage was 5%, the residence time was 20 min, and the magnetic field strength was 200 mT, the recovery rate of iron reached 91.83%, and the iron grade of the recovered products was 67.72%, meeting the level I requirements in GB/T 32545-2016. Based on this result, a process involving SHPS reduction roasting with corncob pyrolysis reducing gas-magnetic separation was established to recover iron from SHPS. This process not only effectively utilizes the iron oxide in SHPS by converting it into iron concentrate powder for the ironmaking industry but also proves that the pyrolysis gas of corncob has good reduction ability.
© 2022 The Authors. Published by American Chemical Society.