Aqueous Zn metal batteries suffer from rapid cycling deterioration due to the severe water corrosion and dendrite growth on Zn anodes. Herein, a highly antiwater Znx-diethylenetriaminepenta(methylene-phosphonic acid) interface layer with good zinc affinity and special nanoscaled 3D granular structure is designed on Zn metal to address these problems. Experimental results combined with theoretical analysis and COMSOL simulations reveal that the hydrophobic groups in such Zn-based organic complex are the decisive factor in preventing H2O from damaging Zn anode surface. The massive Zn2+ attractive sites formed by interaction of methylene-phosphonic acid groups and Zn cause ion channel for fast zinc-ion adsorption and migration. And the developed nano granular architecture on the surface induces redistributed Zn2+ ion flux to realize homogenization with smooth and compact surface deposition. Under the synergism, such modified anodes exhibit long cycling lifespan over 1300 h with a relatively low polarization voltage at 5 mA cm-2. Also, the assembled full cells (including Zn//V2O5 and Zn//MnO2 cell) based on this anode are also demonstrated. The work provides a simple, low cost, and efficient pathway by combining the two concepts of structural design and constructing protective layers on the surface to prepare high-performance Zn anodes toward prospering aqueous zinc-metal batteries.
Keywords: inhibition of side reactions; organic zinc-chelate layer; regulating zinc-ion deposition; zinc affinity; zinc metal battery.