AuPd nanoparticles functionalized core-shell Co3O4/ZnO@ZnO for ultra-sensitive toluene detection

Ziyan Wang; Hongyan Liu; Junkai Shao; Zhenhua Li; Hao Zhang; Caixuan Sun; Guofeng Pan; Xueli Yang

doi:10.1088/1361-6528/ac7475

AuPd nanoparticles functionalized core-shell Co₃O₄/ZnO@ZnO for ultra-sensitive toluene detection

Nanotechnology. 2022 Jun 15;33(36). doi: 10.1088/1361-6528/ac7475.

Authors

Ziyan Wang¹, Hongyan Liu¹, Junkai Shao¹, Zhenhua Li¹, Hao Zhang², Caixuan Sun¹, Guofeng Pan¹, Xueli Yang¹

Affiliations

¹ School of Electronics and Information Engineering, Hebei University of Technology, Tianjin Key Laboratory of Electronic Materials and Devices, Hebei University of Technology, Tianjin 300130, People's Republic of China.
² School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130, People's Republic of China.

PMID: 35636397
DOI: 10.1088/1361-6528/ac7475

Abstract

In this work, core-shell AuPd nanoparticles (NPs) sensitized Co₃O₄/ZnO@ZnO ellipsoid nanoparticles was successfully synthesized via a simple liquid phase synthesis method. SEM and TEM characterization results showed that the as-prepared samples have core-shell ellipsoid morphology and the size of the nanoparticles were uniform. Systematic gas sensing characterization was carried out to obtain the gas sensing property of AuPd NPs decorated Co₃O₄/ZnO@ZnO. It was found that the gas sensing property could be significantly enhanced after noble metal decoration with Au, Pd and AuPd NPs, respectively. The optimal gas sensing performance was achieved by AuPd NPs functionalized Co₃O₄/ZnO@ZnO based gas sensor. The maximum response reached 256-100 ppm toluene at 250 °C, which is 50 °C lower than pure ZnO. The detection limit of AuPd functionalized Co₃O₄/ZnO@ZnO was as low as 100 ppb. The enhanced sensing mechanism was mainly attributed to the synergistic effect of Au and Pd, which was detailly discussed in gas sensing mechanism part.

Keywords: AuPd NPs; ZIF-8; core–shell structure; gas sensor; toluene.