Antibacterial agents derived from conventional organic compounds have traditionally been employed as a biofilm protective coating for many years. These agents, on the other hand, often include toxic components that are potentially hazardous to humans. Multiple approaches have been investigated over the last two decades, including the use of various metallic and oxide materials, in order to produce a diverse variety of usable coating layers. When it comes to material coating approaches, the cold spray technique, which is a solid-state method that works well with nanopowders, has shown superior performance. Its capacity to produce unique material coating in ways that are not possible with other thermal methods is the primary reason for its importance in contemporary production. The present work has been addressed in part to explore the possibility of employing mechanically alloyed Cu50(Ti50-xNix)x; x = 10, 20, 30, and 40 at.% metallic glass powders, for producing an antibiofilm/SUS304 surface protective coating, using the cold spray approach. In this study, elemental Cu, Ti, and Ni powders were low-energy ball milled for 100 h to fabricate metallic glassy powders with different Ni contents. The as-prepared metallic glassy powders were utilized to coat SUS304 sheets, using the cold spraying process. With high nanohardness values, the as-fabricated coating material, in particular Cu50Ti20Ni30, demonstrated remarkable performance in comparison to other materials in its class. Furthermore, it displayed excellent wear resistance while maintaining a low coefficient of friction, with values ranging from 0.32 to 0.45 in the tested range. E. coli biofilms were formed on 20 mm2 SUS304 sheet coated coupons, which had been injected with 1.5 108 CFU mL-1 of the bacterium. With the use of nanocrystalline Cu-based powders, it is feasible to achieve considerable biofilm inhibition, which is a practical strategy for accomplishing the suppression of biofilm formation.
Keywords: antibacterial; high-energy ball milling; metallic glasses; nanoindentation; solid-state coating; thermal stability.