Concrete is a composite material that is commonly used in the construction industry. It will certainly be exposed to fires of varying intensities when used in buildings and industries. The major goal of this article was to look into the influence of mineral additions such as foundry sand and marble dust on the residual characteristics of concrete. To examine the behavior of residual characteristics of concrete after fire exposure, marble dust was substituted for cement and fine sand was substituted for foundry sand in varying amounts ranging from 0% to 20%. It aided in the better disposal of waste material so that it might be used as an addition. The purpose of the experiment was to see how increased temperatures affected residual properties of concrete, including flexural strength, compressive strength, tensile strength, static as well as dynamic elastic modulus, water absorption, mass loss, and ultrasonic pulse velocity. At temperatures of 200 °C, 400 °C, 600 °C, 800 °C, and 1000 °C, the typical fire exposure behavior of concrete was investigated. The effects of two cooling techniques, annealing and quenching, on the residual properties of concrete after exposure to high temperatures were investigated in this study. Replacement of up to 10% of the cement with marble dust and fine sand with foundry sand when concrete is exposed to temperatures up to 400 °C does not influence the behavior of concrete. At temperatures above 400 °C, however, the breakdown of concrete, which includes marble dust and foundry sand, causes a rapid deterioration in the residual properties of concrete, primarily for replacement of more than 10%.
Keywords: annealing; elevated temperature; foundry sand; marble dust; quenching; residual properties of concrete.