There are various factors that may interfere with the activity of biomaterials during endodontic therapy. One of them is the canal system irrigation procedure with different rinsing solutions performed after the placement of bioactive cements. The authors investigate the influence of citric acid, a chelating agent, on the surface and the chemical composition of Biodentine tricalcium silicate-based cement using a multimethod approach. Twenty samples were divided into two groups based on the material setting time. They were subjected to citric acid irrigation with or without ultrasonic activation for 5 and 20 min. The chemical analysis was made with energy dispersive spectroscopy (EDS). The visual assessment of Biodentine surface was carried out in scanning electron microscope (SEM). The volume of material loss during the procedure was measured with Keyence optic microscope and dedicated digital software. Statistical analysis was performed. The results of the study show that the irrigation with citric acid influenced the surface appearance of the material and changed its chemical composition in both investigated groups. The ultrasonic activation (US) of the liquid has also aggravated its impact. Further research is needed to assess if that fact may change the sealing properties of the material influencing the long-term clinical outcome.
Keywords: citric acid; energy dispersive spectroscopy; irrigation; perforation; scanning electron microscope; ultrasonic activation.