An investigation was conducted on the influence that industrial metakaolin waste (IMW) has on the properties of autoclaved fiber cement composition (FCC) samples. FCC samples were made from fiber cement plate's typical components using the same proportions. In samples, IMW was used instead of cement in 10%, 20%, 30% proportions and in 50%, 100% proportions instead of ground quartz. Differential thermal analysis (DTG), thermogravimetric analysis (TGA), ultrasound pulse velocity (UPV), density, porosity and optical microscope (OM) research methods were used to identify the micro and macrostructure of samples. Mechanical properties were evaluated using flexural and compressive strength research methods. It was established that IMW was used instead of cement in fiber cement composition samples up to 10% and in fiber cement composition samples instead of ground quartz forms density microstructure structure because of Al-rich tobermorite. As a result, the flexural and compressive strength increased. Samples with higher content of IMW instead of cement had unreacted IMW and a less dense microstructure. In this case, flexural and compressive strength decreased. All FCC samples were fired in a standard fire curve (ISO 842) for 30 min. Samples of mechanical properties were established by doing flexural and compressive strength tests, and which results showed the same trends.
Keywords: fiber cement; metakaolin; standard fire curve; tobermorite.