Powder-based 3D printing is an excellent technique for the fabrication of complex structural shapes. The outstanding bone remodeling capacity of calcium phosphate bioceramics is a desirable characteristic for such fabrication. Whitlockite (WH) is a calcium phosphate-based ceramic that contains Mg ions and possesses good mechanical properties, rapid resorbability, and promotes osteogenesis. The aim of this study was to fabricate 3D-printed scaffolds using marine plankton-derived WH (MP-WH) powder. The surface morphology and composition of the fabricated scaffolds were characterized by scanning electron microscopy and X-ray diffraction. The biocompatibility and osteogenic effects were evaluated using human mesenchymal stem cells. We successfully obtained a 3D porous scaffold using MP-WH. The MP-WH 3D scaffold showed improved compressive strength compared to the tricalcium phosphate (TCP) 3D scaffold. The in vitro results showed that compared with TCP 3D scaffolds, MP-WH 3D scaffolds were biocompatible and enhanced cell proliferation and adhesion. In addition, alkaline phosphatase activity and real-time polymerase chain reaction assays demonstrated that osteoblast differentiation was improved on the MP-WH scaffold. These results suggest that marine plankton-derived WH is useful for fabricating 3D-printed scaffolds for bone tissue engineering applications.
Keywords: 3-dimensional printing; bone; scaffold; tissue engineering; whitlockite.