PVA/chitosan (PVA/CS) composite hydrogels incorporating silver nanoparticles (AgNPs) were prepared by double-cross-linked procedures: freeze−thawing and electrostatic interactions. Oxalic acid (OA) was used both for solubilization and ionic cross-linking of CS. AgNPs covered by CS (CS-AgNPs) with an average diameter of 9 nm and 18% silver were obtained in the presence of CS, acting as reducing agent and particle stabilizer. The increase of the number of freeze−thaw cycles, as well as of the PVA:CS and OA:CS ratios, resulted in an increase of the gel fraction and elastic modulus. Practically, the elastic modulus of the hydrogels increased from 3.5 kPa in the absence of OA to 11.6 kPa at a 1:1 OA:CS weight ratio, proving that OA was involved in physical cross-linking. The physicochemical properties were not altered by the addition of CS-AgNPs in low concentration; however, concentrations higher than 3% resulted in low gel fraction and elastic modulus. The amount of silver released from the composite hydrogels is very low (<0.4%), showing that AgNPs were well trapped within the polymeric matrix. The composite hydrogels displayed antimicrobial activity against S. aureus, K. pneumoniae or P. gingivalis. The low cytotoxicity and the antibacterial efficacy of hydrogels recommend them for wound and periodontitis treatment.
Keywords: PVA/chitosan hydrogels; antibacterial; eco-friendly; oxalic acid; silver nanoparticles.