The in situ combustion (ISC) technique is promisingly applied in heavy oil recovery, whereas the operation inevitably causes high temperature and high pressure for a long duration in the thermal recovery well. As a critical component, oil casing, traditionally made of plain carbon steel in China, generally suffers from poor creep resistance and degraded remnant strength under such a harsh environment, which leads to frequent casing damage and inferior recovery efficiency. In this study, a strategy was adopted to tackle the issue by adding chromium (Cr) element into the plain carbon steel. We designed two types of novel steel with the respective addition of 1 wt.% and 13 wt.% Cr element into plain carbon steel for oil casing. Surprisingly, the trace addition of Cr element with 1 wt.% effectively lowered the creep rate in a creep test at 600 °C and 400 MPa and maintained high remnant tensile strength after creep. More significantly, prior creep history dramatically enhanced remnant strength when Cr element was added up to 13 wt.%. After a long-term creep time of 96 h, the samples were conferred by a stress increment of ~92.5 MPa (~11.0%) relative to the creep-free counterparts, whereas the value was reduced by ~158.4 MPa (~17.8%) for plain carbon steel under the same deformation conditions. Such superior mechanical performances in the Cr-doped steels are mainly ascribed to precipitation retardation of carbides and sluggish precipitate coarsening, which continuously favors a precipitation-strengthening effect in steel. These findings provide a fundamental understanding of precipitation response and creep behaviors and, more importantly, enable the development of high-performance steels used in the field of unconventional petroleum and gas resources.
Keywords: carbides; creep; microstructures; steels; strength.