The resistance of microorganisms to antibiotics is a crucial problem for which the application of nanomaterials is among a growing number of solutions. The aim of the study was to create a nanocomposite (composed of graphene oxide and silver nanoparticles) with a precise mode of antibacterial action: what enables textiles to be coated in order to exhibit antibacterial properties. A characterization of nanomaterials (silver nanoparticles and graphene oxide) by size distribution, zeta potential measurements, TEM visualization and FT-IR was performed. The biological studies of the nanocomposite and its components included the toxicity effect toward two pathogenic bacteria species, namely Pseudomonas aeruginosa and Staphylococcus aureus, interaction of nanomaterials with the outer layer of microorganisms, and the generation of reactive oxygen species and lipid peroxidation. Afterwards, antibacterial studies of the nanocomposite's coated textiles (cotton, interlining fabric, polypropylene and silk) as well as studies of the general toxicity towards a chicken embryo chorioallantoic membrane model were conducted. The toxicity of the nanocomposite used was higher than its components applied separately (zones of growth inhibition for P. aeruginosa for the final selected concentrations were as follows: silver nanoparticles 21 ± 0.7 mm, graphene oxide 14 ± 1.9 mm and nanocomposite 23 ± 1.6 mm; and for S. aureus were: silver nanoparticles 27 ± 3.8 mm, graphene oxide 14 ± 2.1 mm, and nanocomposite 28 ± 0.4 mm. The viability of P. aeruginosa and S. aureus after treatment with selected GO-Ag decreased to 27% and 31%, respectively, compared to AgNPs, when the viability of both species was 31% and 34%, accordingly). The coated textiles showed encouraging antibacterial features without general toxicity towards the chicken embryo chorioallantoic membrane model. We demonstrated that graphene oxide might constitute a functional platform for silver nanoparticles, improving the antibacterial properties of bare silver. Due to the application of the nanocomposite, the textiles showed promising antibacterial features with a low general toxicity, thereby creating a wide possibility for them to be used in practice.
Keywords: antibacterial; coating; graphene oxide; nanocomposite; silver nanoparticles.