In order to optimize the process parameters of Si-Si wafer direct bonding at room temperature, Si-Si surface activated bonding (SAB) was performed, and the effect of the argon ion beam current for surface activation treatment on the Si-Si bonding quality was investigated. For the surface activation under the argon ion beam irradiation for 300 s, a smaller ion beam current (10~30 mA) helped to realize a lower percentage of area covered by voids and higher bonding strength. Especially with the surface activation under 30 mA, the bonded Si-Si specimen obtained the highest bonding quality, and its percentage of area covered by voids and bonding strength reached <0.2% and >7.62 MPa, respectively. The transmission electron microscopy analyses indicate that there exists an ultrathin amorphous Si interlayer at the Si-Si bonding interface induced by argon ion beam irradiation to Si wafer surfaces, and its thickness increases as the argon ion beam current rises. The investigation results can be used to optimize the SAB process and promote the applications of SAB in the field of semiconductor devices.
Keywords: Ar ion beam irradiation; bonding interface; room-temperature Si-Si bonding; surface activated bonding.