Cement production is environmentally unsustainable due to the high anthropogenic carbon emissions produced. Supplementary cementitious materials (SCMs), derived from the by-products of different industries, have been deemed an effective way to reduce carbon emissions. The reduction in carbon emissions is achieved by lowering the clinker factor of cement, through a partial replacement with an SCM. Sugarcane Bagasse Ash (SCBA) is produced as an agricultural waste from the sugarcane industry and has gained a lot of attention for being a feasible and readily available pozzolanic material, underutilised as an SCM. This study evaluates alkali-activated sugarcane bagasse ash's mechanical and durability performance, at varied contents, in binary blended cement concrete and ternary blended cement concrete containing silica fume (SF). Potassium Hydroxide (KOH), used as the alkali activator, is intended to enhance the reactivity of the ash, with the possibility of a high-volume SCBA content. The mechanical performance was investigated by compressive and split tensile strength tests, and durability performance was investigated using the Oxygen Permeability Index (OPI) test. In addition, a micro-CT porosity test was conducted to assess how the microstructure and porosity of the concrete affect the mechanical and durability performance. The results indicated that using SCBA in a ternary blend with SF can significantly improve the overall performance and create less porous concrete. At 30% SCBA and 10% SF replacement, the performance tests revealed the highest mechanical strength and the lowest permeability, outperforming the control concrete and the binary blended cement concrete containing only SCBA.
Keywords: compressive strength; durability; oxygen permeability index; silica fume; sugarcane bagasse ash.