Enabling a biodegradable polymer radiopaque under X-ray is much desired for many medical devices. Physical blending of a present biodegradable polymer and a commercialized medical contrast agent is convenient yet lacks comprehensive fundamental research. Herein, we prepared a biodegradable polymer-based radiopaque raw material by blending poly(l-lactic acid) (PLLA or simply PLA) and iohexol (IHX), where PLA constituted the continuous phase and IHX particles served as the dispersed phase. The strong X-ray adsorption of IHX enabled the composite radiopaque; the hydrolysis of the polyester and the water solubility of the contrast agent enabled the composite biodegradable in an aqueous medium. The idea was confirmed by in vitro characterizations of the resultant composite, in vivo subcutaneous implantation in rats up to 6 months, and the clear visualization of a part of a biodegradable occluder in a Bama piglet under X-ray. We also found that the crystallization of PLA was significantly enhanced in the presence of the solid particles, which should be taken into consideration in the design of an appropriate biomaterial composite because crystallization degree influences the biodegradation rate and mechanical property of a material to a large extent. We further tried to introduce a small amount of poly(vinylpyrrolidone) into the blend of PLA and IHX. Compared to the bicomponent composite, the tricomponent one exhibited decreased modulus and increased elongation at break and tensile strength. This paves more ways for researchers to select appropriate raw materials according to the regenerated tissue and the application site.
Keywords: biodegradable polymer; biomaterial; composite; poly(L-lactic acid); radiopaque; spherulite.