Perpendicular shape anisotropy (PSA) offers a practical solution to downscale spin-transfer torque magnetoresistive random-access memory (STT-MRAM) beyond the sub-20 nm technology node while retaining thermal stability. However, our understanding of the thermomagnetic behavior of PSA-STT-MRAM is often indirect, relying on magnetoresistance measurements and micromagnetic modeling. Here, the magnetism of a NiFe PSA-STT-MRAM nanopillar is investigated using off-axis electron holography, providing spatially resolved magnetic information as a function of temperature. Magnetic induction maps reveal the micromagnetic configuration of the NiFe storage layer (∼60 nm high, ≤20 nm diameter), confirming the PSA induced by its 3:1 aspect ratio. In situ heating demonstrates that the PSA of the storage layer is maintained up to at least 250 °C, and direct quantitative measurements reveal a moderate decrease of magnetic induction. Hence, this study shows explicitly that PSA provides significant stability in STT-MRAM applications that require reliable performance over a range of operating temperatures.
Keywords: Perpendicular shape anisotropy STT MRAM; nanomagnetism; off-axis electron holography; thermomagnetic stability.