Background: Denture stomatitis has been linked to the adhesion and proliferation of Candida albicans (C. albicans) on denture bases, which is a common and recurrent problem in denture wearers. The current study aimed to evaluate the effect of incorporating caffeic acid phenethyl ester (CAPE) into autopolymerized polymethyl methacrylate (PMMA) acrylic resin on C. albicans adhesion, surface roughness, and hardness as well as the correlation between tested properties.
Methods: Autopolymerized acrylic resin discs (N = 100, 50/C. albicans adhesion; 50/C. albicans surface roughness and hardness test) were fabricated in dimensions 15 × 2.5 mm, samples were categorized into 5 groups (n = 10) based on CAPE concentrations; unmodified (control), 2.5, 5, 10 and 15% wt of acrylic powder. Specimens were stored in distilled water for 48 h at 37°C. C. albicans adhesion was evaluated via direct culture method. Profilometer and Vickers hardness tester were used for surface roughness and hardness measurement. Post hoc Tukey's HSD with ANOVA test was performed to compare the difference of means amongst groups. P values were statistically significant at ≤0.05.
Results: The addition of 2.5% of CAPE to PMMA has significantly reduced C. albicans counts in comparison to higher CAPE concentrations (p < 0.001). As for surface roughness, it was noticed that it increased with increased CAPE concentrations (p < 0.0001). While surface hardness decreased as CAPE concentrations increased (p < 0.0001). All tested properties showed a significant difference amongst groups for C. albicans colony count and surface parameters.
Conclusion: The addition of 2.5% of CAPE to PMMA acrylic resin significantly decreased C. albicans count compared to higher CAPE concentrations. CAPE can be used as an adjunct in the prevention of DS by incorporating in the PMMA acrylic resin.
Copyright © 2022 Khalifa S. Al-Khalifa et al.