This study introduced binary nanoparticle (NP) inclusions into a biomedical-grade photosensitive resin (Biomed Clear-BC). Multi-functional, three-dimensional (3D) printed objects were manufactured via the vat photopolymerization additive manufacturing (AM) technique. Cellulose nanofibers (CNFs) as one dimensional (1D) nanomaterial have been utilized for the mechanical reinforcement of the resin, while three different spherical NPs, namely copper NPs (nCu), copper oxide NPs (nCuO), and a commercial antimicrobial powder (nAP), endowed the antimicrobial character. The nanoparticle loading was kept constant at 1.0 wt.% to elucidate any synergistic effects as a function of the filler loading. Raman, thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC) revealed the chemical/spectroscopic and thermal properties of the different manufactured samples. Scanning electron microscopy and Atomic Force Microscopy (AFM) revealed the morphology of the samples. Mechanical properties revealed the reinforcement mechanisms, namely that BC/CNF (1.0 wt.%) exhibited a 102% and 154% enhancement in strength and modulus, respectively, while BC/CNF(1.0 wt.%)/AP(1.0 wt.%) exhibited a 95% and 101% enhancement, as well as an antibacterial property, which was studied using a screening agar well diffusion method. This study opens the route towards novel, multi-functional materials for vat photopolymerization 3D printing biomedical applications, where mechanical reinforcement and antibacterial performance are typically required in the operational environment.
Keywords: antibacterial; biomedical; cellulose nanofiber (CNF); copper (Cu); copper oxide (Cu2O); nanocomposite; vat photopolymerization.