Electroactive Co(iii) salen metal complexes and the electrophoretic deposition of their porous organic polymers onto glassy carbon

Marcello B Solomon; Aditya Rawal; James M Hook; Seth M Cohen; Clifford P Kubiak; Katrina A Jolliffe; Deanna M D'Alessandro

doi:10.1039/c8ra04385j

Electroactive Co(iii) salen metal complexes and the electrophoretic deposition of their porous organic polymers onto glassy carbon

RSC Adv. 2018 Jul 3;8(43):24128-24142. doi: 10.1039/c8ra04385j. eCollection 2018 Jul 2.

Authors

Marcello B Solomon¹, Aditya Rawal², James M Hook², Seth M Cohen³, Clifford P Kubiak³, Katrina A Jolliffe¹, Deanna M D'Alessandro¹

Affiliations

¹ School of Chemistry, The University of Sydney New South Wales 2006 Australia deanna.dalessandro@sydney.edu.au kate.jolliffe@sydney.edu.au +61 2 9351 3329 +61 2 9351 3777.
² NMR Facility, Mark Wainwright Analytical Centre, The University of New South Wales 2052 Australia.
³ Department of Chemistry and Biochemistry, University of California San Diego California 92093 USA.

Abstract

This paper reports the CO₂ electroreduction properties of three bis-bromo Co(iii) salen metal complexes and their Porous Organic Polymers (POPs) as a platform for using the salen core as a multi-electron reducing agent. Although Co(iii) salen metal complexes have been studied extensively for their chemical catalysis with CO₂, their electrochemical behaviour, particularly their reduction, in the presence of CO₂ is much less explored. The discrete Co(iii) complexes enabled the reduction of CO₂ to CO in faradaic efficiencies of up to 20%. The reductive electrochemical processes of Co(iii) salen complexes are relatively unknown; therefore, the mechanism of reduction for the complexes was investigated using IR and UV-Vis-NIR spectroelectrochemical (SEC) techniques. The discrete bis-bromo salen complexes were incorporated into POPs with tris-(p-ethynyl)-triphenylamine as a co-ligand and were characterised using solid state NMR, IR, UV-Vis-NIR and Field Emission Scanning Electron Microscopy (FE-SEM). The POP materials were electrophoretically deposited onto glassy carbon under milder conditions than those previously reported in the literature. Direct attachment of the POP materials to glassy carbon enabled improved solid state electrochemical analysis of the samples. The POP materials were also analysed via SEC techniques, where a Co(ii/i) process could be observed, but further reductions associated with the imine reduction compromised the stability of the POPs.