Magnetic molecularly imprinted nanoparticles (MMINPs) were obtained with a one-step process through miniemulsion self-assembly using an amphiphilic random copolymer as both an emulsifier and MMINP coating, oleic acid-modified magnetite nanoparticles as magnetic cores, and melamine (MEL) as the template molecule. MMINPs were assembled under an external magnetic field to construct photonic crystal (PC) sensor for naked-eye detection of MEL. The MMINPs were characterized by FT-IR, TEM, TGA, and VSM. The analytical performances of the magnetic molecularly imprinted PC sensor for MEL (MEL-MMIPCs) were investigated with respect to sensitivity, response time, selectivity, and stability. As the MEL concentration increases from 1.0 to 1.0 × 106 μg/l, the reflection wavelength of MEL-MMIPCs shifted from 497 to 709 nm, and was linear with the logarithm of MEL concentration in this range. The detection limit was 0.21 μg/l (S/N = 3) and response time was within 30 s. The MEL-MMIPC sensor had an imprinting factor of 5.09, and selectivity factors for the analogs cyanuric acid and atrazine were 8.76 and 5.75, respectively, indicating the high sensitivity and selectivity. After 10 cycles of elution/response, MEL-MMIPCs still had a good ability to recognize MEL.
Keywords: Magnetic colloidal nanoparticles; Magneto-responsive photonic crystal; Melamine; Molecular imprinting technology.
© 2022. The Author(s), under exclusive licence to Springer-Verlag GmbH Austria, part of Springer Nature.