Final irrigation protocols affect radicular dentin DMP1-CT expression, microhardness, and biochemical composition

Abstract

Objective: To evaluate the effect of several final irrigation protocols on radicular dentin microhardness, biochemical composition, and DMP1-CT expression.

Materials and methods: A total of 140 single-rooted human teeth were prepared with WaveOne Gold files and randomly distributed into 7 groups (n = 20) according to the final irrigation protocol: distilled water (DW); sodium hypochlorite-EDTA (NaOCl-EDTA); EDTA (EDTA); EDTA-NaOCl (EDTA-NaOCl); EDTA-chlorhexidine (EDTA-CHX); passive ultrasonic irrigation (PUI:NaOCl-EDTA); and PUI:NaOCl-EDTA-NaOCl. Dentin microhardness (n = 10) was evaluated in the root canal lumen using Vickers hardness tester. Immunohistochemical analysis (n = 5) was used to evaluate DMP1-CT expression. Dentin ultrastructure and biochemical composition were evaluated by using Raman and energy dispersive X-ray analysis (EDAX) (n = 5) with a scanning electron microscope (SEM). Analysis of variance (ANOVA) and Tukey test were performed (p˂0.05).

Results: Raman spectra of the organic content and DMP1-CT expression were lower at the lumen canal in EDTA-NaOCl, PUI:NaOCl-EDTA, and PUI:NaOCl-EDTA-NaOCl when compared to control (p < 0.05). EDAX showed reduced values for calcium and phosphorus in EDTA-NaOCl, PUI:NaOCl-EDTA, and PUI:NaOCl-EDTA-NaOCl. SEM microphotography's showed completely cleaned dentin, permeable tubules, and dentin erosion, mainly when PUI was used. NaOCl-EDTA presented significantly higher microhardness values than PUI:NaOCl-EDTA-NaOCl (p < 0.05). PUI:NaOCl-EDTA-NaOCl exhibited the lowest Vickers hardness values of all groups.

Conclusion: The final irrigation protocols that used a final rinse with NaOCl and PUI showed a detrimental effect on radicular dentin DMP1-CT expression, biochemical composition, and microhardness.

Clinical relevance: The adequate irrigation protocol could be advantageous to preserve the radicular dentin ultrastructure, promote adequate adhesion, and sustain favorable conditions for biomineralization and regeneration.

Keywords: DMP1-CT; Irrigation protocols; Microhardness; Non-collagenous proteins.