Solid-state electrolytes (SSEs) hold a critical role in enabling high-energy-density and safe rechargeable batteries with Li metal anode. Unfortunately, nonuniform lithium deposition and dendrite penetration due to poor interfacial solid-solid contact are hindering their practical applications. Here, solid-state lithium naphthalenide (Li-Naph(s)) is introduced as a plastic monolithic mixed-conducting interlayer (PMMCI) between the garnet electrolyte and the Li anode via a facile cold process. The thin PMMCI shows a well-ordered layered crystalline structure with excellent mixed-conducting capability for both Li+ (4.38 × 10-3 S cm-1 ) and delocalized electrons (1.01 × 10-3 S cm-1 ). In contrast to previous composite interlayers, this monolithic material enables an intrinsically homogenous electric field and Li+ transport at the Li/garnet interface, thus significantly reducing the interfacial resistance and achieving uniform and dendrite-free Li anode plating/stripping. As a result, Li symmetric cells with the PMMCI-modified garnet electrolyte show highly stable cycling for 1200 h at 0.2 mA cm-2 and 500 h at a high current density of 1 mA cm-2 . The findings provide a new interface design strategy for solid-state batteries using monolithic mixed-conducting interlayers.
Keywords: dendrite-free; lithium aromatic hydrocarbon complex; mixed-conducting interlayer; solid-solid interface; solid-state electrolyte.
© 2022 The Authors. Advanced Science published by Wiley-VCH GmbH.