Transparent glass ceramics (GCs) containing Ba4Yb3F17:Er3+ nanocrystals were successfully fabricated by a traditional melt-quenching method. The formation of Ba4Yb3F17 nanocrystals was confirmed by X-ray diffraction, transmission electron microscopy, and selected area electron diffraction. Compared with the precursor glass, the enhanced emission intensity and lifetime of GCs indicate that the Er3+ ions incorporate into the Ba4Yb3F17 nanocrystals after crystallization. The color tuning properties with doping under 980 nm excitation have been systematically discussed. It was found that the red/green ratio increased with Er3+ ion doping and the corresponding color changed from greenish-yellow to yellow-green. Furthermore, the temperature-dependent luminescence properties were studied in detail by the fluorescence intensity ratio (FIR) technique. The monotonic change of FIR with temperature indicates that this material is suitable for temperature sensing. At a temperature of 450 K, the relative sensitivity of the prepared sample reached its maximal value of 0.20% K-1. The results show that the GCs containing Ba4Yb3F17:Er3+ nanocrystals are candidate materials for temperature sensing.
This journal is © The Royal Society of Chemistry.