Over the past decades, there has been extensive study on the design of porous bioceramic scaffolds with controlled bioactivity and biodegradation in bone tissue repair. A variety of suggestive models and concepts have been proposed with regard to the role of microstructure and composition of biomaterials which affect new bone tissue growth. However, it is a challenge to fabricate functional scaffolds with the desired physiological properties and osteogenic potentials that is comparable to the bone's natural healing time scale. We demonstrate a one-step versatile fabrication of a single-phase and homogenously mixed bioactive load-bearing scaffolds (Sr-CS, CaSiO3/Ca2SiO4, and CaP) with superior biological properties in a critical size bone defect (Ø ~ 6.0 × 8.0 mm). In vivo study revealed the CaSiO3/Ca2SiO4 scaffold had the best amount of new bone growth and osteogenic repair. The Sr-CS exhibited an adequate pore network for rapid inorganic exchange and moderate mechanical stability; however, the CaSiO3/Ca2SiO4 saw over-fast resorption and mass loss compared to the Sr-CS and CaP. On the other hand, the CaP scaffold saw mechanically outstanding elastroplastine and stability but had limited biodegradation of its constructs which retarded new cancellous bone growth. The CaSiO3/Ca2SiO4 group saw superior acceleration and formation of mineralized new bone tissues in the defect. Moreover, the CaSiO3/Ca2SiO4 showed appreciable decay of the biomaterials beneficial for osteogenic cell activity. The dramatic stimulation of bone repair and angiogenesis with the CaSiO3/Ca2SiO4 suggests a promising application of this novel bioactive scaffold in the repair of skeletal defects. Systemic representation of the fabricated microspheres with in vivo and in vitro study analysis.
Keywords: Healing time scale; Load-bearing scaffold; Osteogenic cell activity; Single phase scaffold.
© 2022. International Federation for Medical and Biological Engineering.