A ferromagnetic metal nanolayer with a large perpendicular magnetic anisotropy, small saturation magnetization, and small magnetic damping constant is a crucial requirement for high-speed spintronic devices. Fabrication of these devices on Si/SiO2 amorphous substrates with polycrystalline structure is also strongly desired for the mass production industry. This study involves the investigation of sub-terahertz (THz) magnetization precessional motion in a newly developed material system consisting of Cu2 Sb-type MnAlGe and (Mn-Cr)AlGe films by means of an all-optical pump-probe method. These materials exhibit large perpendicular magnetic anisotropy in regions of a few nanometers in size. The pseudo-2D crystal structures are clearly observed in the high-resolution transmission electron microscopy (TEM) images for the film samples grown on thermally oxidized silicon substrates. The TEM images also show a partial substitution of Cr atoms for the Mn sites in MnAlGe. A magnetization precession frequency of 0.164 THz with a relatively small effective magnetic damping constant of 0.012 is obtained for (Mn-Cr)AlGe. Theoretical calculation infers that the modification of the total density of states by Cr substitution decreases the intrinsic magnetic damping constant of (Mn-Cr)AlGe.
Keywords: all-optical methods; perpendicular magnetic anisotropy; terahertz spintronics; ultrathin films.
© 2022 The Authors. Small published by Wiley-VCH GmbH.