Preparation of Ag3PO4/α-Fe2O3 hybrid powders and their visible light catalytic performances

Abstract

The inefficiency of conventional photocatalytic treatment for removing rhodamine B is posing potential risks to ecological environments. Here, we construct a highly efficient photocatalyst consisting of Ag₃PO₄ and α-Fe₂O₃ hybrid powders for the treatment of rhodamine B. Ag₃PO₄ nanoparticles (nanoparticles, about 50 nm) are uniformly dispersed on the surface of α-Fe₂O₃ microcrystals (hexagonal sheet, about 1.5 μm). The Ag₃PO₄-deposited uniformity on the α-Fe₂O₃ surface first increased, then decreased on increasing the hybrid ratio of Ag₃PO₄ to α-Fe₂O₃. When the hybrid ratio of Ag₃PO₄ to α-Fe₂O₃ is 1 : 2, the distribution of Ag₃PO₄ particles on the sheet α-Fe₂O₃ is more uniform with excellent Ag₃PO₄/α-Fe₂O₃ interface performance. The catalytic degradation efficiency of hybrids with the introduction of Ag₃PO₄ nanoparticles on the α-Fe₂O₃ surface reached 95%. More importantly, the hybrid material exhibits superior photocatalytic stability. Ag₃PO₄/α-Fe₂O₃ hybrids have good reusability, and the photocatalytic efficiency could still reach 72% after four reuses. The excellent photocatalytic activity of the as-prepared hybrids can be attributed to the heterostructure between Ag₃PO₄ and α-Fe₂O_3, which can effectively inhibit the photoelectron-hole recombination and broaden the visible light response range.