Three titanium (Ti) targets with different purities were used to prepare Ti films on polyimide substrates by DC magnetron sputtering. The microstructures of Ti films were characterized by a metallographic microscope, X-ray diffractometer, field emission scanning electron microscope and three-dimensional surface topography instrument. In this study, we investigated the effects of Ti target purity and microstructure on film deposition rate, surface roughness, microstructure and resistivity. The results show that the deposition rate increased with increasing Ti target purity. Ti film deposited by the high-purity (99.999%) Ti target has fewer surface particles with smaller size, lower surface roughness and lower resistivity when compared to that prepared by the Ti target of low purity (99.7%). The surface roughness of Ti film prepared by the high-purity Ti target was Sa = 121 nm, the deposition rate was 16.3 nm/min and the resistivity was 6.9 × 10-6 Ω·m. For Ti targets of the same purity, the performance of Ti film prepared by a target with equiaxed α-phase grains is better than that of Ti film prepared by a target with twins and β-phase grains.
Keywords: Ti target; deposition rate; microstructure; purity; resistivity.