Bisphenol A-glycidyl methacrylate (bis-GMA) and urethane dimethacrylate (UDMA) are usually combined with low-viscosity monomers to obtain more desirable viscosity, handling characteristics and general properties. The present study determined the flexural strength (FS), flexural modulus (FM), diametral tensile strength (DTS), and hardness (HV) of five matrices and composites based on these resins. The polymerization shrinkage stress (PSS) was also studied for the composites. The polymer matrices were formed using bis-GMA and UDMA. TEGDMA, HEMA and HDDMA acted as co-monomers. The composites had 45 wt.% of filler content. The highest FS and FM were obtained from the UDMA/bis-GMA/TEGDMA/HEMA matrix and the composite (matrix + filler). The best DTS values were obtained from the UDMA/bis-GMA/HEMA matrix and the composite. One of the lowest values of FS, FM, and DTS was obtained from the UDMA/bis-GMA/HDDMA matrix and the composite. All the composites demonstrated similar hardness values. The lowest polymerization shrinkage stress was observed for the UDMA/bis-GMA/TEGDMA/HEMA composite, and the highest PSS was observed for the UDMA/bis-GMA/TEGDMA/HDDMA composite. The addition of HEMA had a positive effect on the properties of the tested materials, which may be related to the improved mobility of the bis-GMA and UDMA monomers.
Keywords: HDDMA; HEMA; TEGDMA; UDMA; bis-GMA; dental composites; dental resins; hardness; mechanical properties; shrinkage stress.