This paper aims to study the suitability of partial replacement of lime by waste originating from the cleaning of flue gases from the combustion of industrial wastes in the production of autoclaved aerated concrete (AAC). The compressive strength, bulk density, pore structure, phase composition, and microstructure of hydration products of the AAC were analyzed. According to the results, the addition of the waste can effectively enhance the mechanical properties of AAC due to the differences in morphology of hydration product-1.1 nm tobermorite and related dense microstructure. The pore size distribution was significantly influenced by waste addition, which was one of the main reasons for the increase in thermal conductivity. The XRD and SEM results showed that foreign ions introduced with the wastes affect the synthesis of 1.1 nm tobermorite. Moreover, it was shown that waste containing a high content of CaO can be used as lime replacement, which allows reducing CO2 emissions during the AAC production process.
Keywords: 1.1 nm tobermorite; CO2 emission; autoclaved aerated concrete; calcareous waste; calcium silicate hydrates.