The development of new chemically resistant anodes for protonic ceramic fuel cells (PCFCs) is urgently required to avoid the costly deep hydrogen purification method. Ba0.95Ca0.05Ce0.9Y0.1O3-δ (5CBCY), which is more chemically resistant than BaCaCe0.9Y0.1O3-δ, was here tested as a component of a composite NiO-5CBCY anode material. A preparation slurry comprising 5CBCY, NiO, graphite, and an organic medium was tape cast, sintered and subjected to thermal treatment in 10 vol.% H2 in Ar at 700 °C. Differential thermal analysis, thermogravimetry, quadrupole mass spectrometry, X-ray diffraction analysis, scanning electron microscopy, the AC four-probe method and electrochemical impedance spectroscopy were used for the investigation. The electrical conductivity of the Ni-5CBCY in H2-Ar at 700 °C was 1.1 S/cm. In the same gas atmosphere but with an additional 5 vol.% CO2, it was slightly lower, at 0.8 S/cm. The Ni-5CBCY cermet exhibited repeatable electrical conductivity values during Ni-to-NiO oxidation cycles and NiO-to-Ni reduction in the 5CBCY matrix, making it sufficient for preliminary testing in PCFCs.
Keywords: BCY; anode; cermet; high-temperature protonic ceramic fuel cells; tape casting.