Tubular composites are widely used in many industrial applications, and there is need to use new material and reliable manufacturing processes to improve the performance and process aspects. The current research presents a detailed study to understand the flexure response of rectangular tubular composites based on thin ply carbon fibres and Elium® resin. Another aim was to understand the failure mechanisms of novel tubular thermoplastic composite systems and carry out a baseline comparison with Epoxy-based tubular systems. In the current research, a bladder-assisted resin transfer moulding process was used to manufacture hollow thermoplastic composite tubes, and the bending behaviour of thin ply carbon (TPC) composite parts with novel Elium® (EL) and Epoxy (EP) resin as the matrix material was studied using a detailed experimental study. A testing method with optimized support span and a saddle was used to carry out three-point bending tests on the tubular composite structures. The TPC/EL composite tubes have shown 10% higher bending strength, with a noticeable increase in deformation due the presence of extended plasticity attributes for acrylic Elium resin. Failure mechanisms studied with the detailed microscopic investigation have shown severe catastrophic failure for epoxy-based composite tubes; however, acrylic Elium®-based composite tubes have shown different damage modes such as fibre splitting, resin infragmentation, and fibre resin-interfacial cracking.
Keywords: bending; failure mechanisms; hollow composite tubes; thermoplastic resin.