Suture is an important part of surgery, and wounds closing after surgery remains a challenge for postoperative care. Currently, silk, linen fiber, and cotton are available in the market as non-absorbable suture biomaterials. So, there is an urgent need to develop a novel suture with advantageous characteristics compared to the ones available on the market. In present study, a series of ultra-high molecular weight chitosan with different DD and MV were prepared from squid cartilage by alkaline treatment and ultrasonic degradation. The corresponding chitosan monofilaments were prepared by a wet spinning process and were characterized as sutures. The effects of the DD and MV of chitosan on the properties of its monofilament were studied, including surface morphology, mechanical property, swelling ratio, ash content, in vitro enzymatic degradation, and in vitro cytotoxicity. According to the results, AS-85 was chosen to be the best suitable as an absorbable surgical suture, which was spun from squid cartilage chitosan with DD~85% and MV~1.2 × 106. The outcome of the present study might derive tremendous possibilities for the utilization of squid cartilage β-chitin for biomedical applications.
Keywords: absorbable surgical suture; degree of deacetylation; squid cartilage chitosan; viscosity average molecular weight; wet spinning.