Pressure response of decylammonium-containing 2D iodide perovskites

Marta Morana; Rossella Chiara; Boby Joseph; Thomas B Shiell; Timothy A Strobel; Mauro Coduri; Gianluca Accorsi; Ausonio Tuissi; Angelica Simbula; Federico Pitzalis; Andrea Mura; Giovanni Bongiovanni; Lorenzo Malavasi

doi:10.1016/j.isci.2022.104057

Pressure response of decylammonium-containing 2D iodide perovskites

iScience. 2022 Mar 11;25(4):104057. doi: 10.1016/j.isci.2022.104057. eCollection 2022 Apr 15.

Authors

Affiliations

¹ Department of Chemistry and INSTM, Viale Taramelli 16, 27100 Pavia, Italy.
² Elettra-Sincrotrone Trieste S. C. P. A., S.S. 14 km 163.5 in Area Science Park, Basovizza, Trieste, Italy.
³ Earth and Planets Laboratory, Carnegie Institution for Science, Washington, DC 20015, USA.
⁴ CNR Nanotec, Institute of Nanotechnology, c/o Campus Ecotekne, via Monteroni, 73100 Lecce, Italy.
⁵ CNR-Consiglio Nazionale Delle Ricerche, Istituto di Chimica Della Materia Condensata e di Tecnologie per L'Energia, Via Previati 1/e, 23900 Lecco, Italy.
⁶ Department of Physics, University of Cagliari, Cittadella Universitaria S.P. Monserrato-Sestu km 0.7, 09042 Monserrato, Italy.

Abstract

Manipulation by external pressure of the optical response of 2D Metal Halide Perovskites (MHPs) is a fascinating route to tune their properties and promote the emergence of novel features. We investigate here DA₂PbI₄ and DA₂GeI₄ (DA = decylammonium) perovskites in the pressure range up to ∼12 GPa by X-ray powder diffraction, absorption, and photoluminescence spectroscopy. Although the two systems share a similar structural evolution with pressure, the optical properties are rather different and influenced by Pb or Ge. DA₂PbI₄ shows a progressive red shift from 2.28 eV (P = 0 GPa) to 1.64 eV at 11.5 GPa, with a narrow PL emission, whereas DA₂GeI₄, changes from a non-PL system at ambient pressure to a clear broadband emitter centered around 730 nm with an intensity maximum at about 3.7 GPa. These results unveil the role of the central atom on the nature of emission under pressure in 2D MHPs containing a long alkyl chain.

Keywords: Engineering; Materials characterization; Materials chemistry; Materials physics.