In this work, metal halide perovskite quantum dots (QDs) with Formamidinium (FA) and Cs mixed cations were fabricated using a solution-processed method at room temperature. By controlling Cs doping ratios in a precursor, the optical properties of mixed-cation perovskite QDs were systematically studied. With the increase in Cs ion doping, the photoluminescence (PL) spectra of perovskite QDs were blueshifted, which was mainly due to the smaller radius of Cs ions than those of FA. Temperature-dependent PL spectra were conducted on mixed-cation perovskite QDs. As the temperature gradually increased from 4 K to 300 K, PL peaks were blue shifted, and full-width at half maximum (FWHM) was widened, which was directly related to lattice thermal expansion and the carrier-photon coupling effect under temperature variation. At the same time, excess Cs ion doping had a prominent influence on optical properties at low temperatures, which was mainly due to the introduction of detrimental defects in perovskite crystals. Therefore, it is particularly important to control doping concentration in the preparation of high-quality perovskite QDs and efficient photoelectric devices.
Keywords: low-temperature PL; mixed-cation doping; perovskite quantum dots.